Monel K500 Rod – Superior Corrosion Resistance & High Mechanical Strength for Marine, Petrochemical & Aerospace Systems
Description
Monel K500 rod is a precipitation-hardened nickel-copper alloy designed to deliver exceptional corrosion resistance, high tensile strength, and durability in the most aggressive industrial environments. Composed of 63–67% nickel, 27–33% copper, with additions of aluminum (2.3–3.15%) and titanium (0.35–0.85%), this alloy combines the corrosion resistance of Monel 400 with enhanced mechanical properties through γ' phase (Ni₃(Al,Ti)) precipitation hardening.
Ideal for marine, oil & gas, and aerospace applications, Monel K500 rods achieve a tensile strength of 1,100–1,300 MPa and yield strength of 800–1,000 MPa after aging treatment, outperforming conventional stainless steels in high-stress and corrosive conditions. Its resistance to chloride-induced pitting, stress corrosion cracking (SCC), and sulfidation in H₂S-rich environments makes it indispensable for subsea components, sour gas well tools, and seawater pump shafts. With a melting range of 1,288–1,343°C and near-zero magnetic permeability even at cryogenic temperatures (-196°C), it ensures reliability in extreme thermal, chemical, and electromagnetic conditions.
Technical Specifications (Table)
| Property |
Value |
Standard |
| Chemical Composition |
Ni: 63–67%, Cu: 27–33%, Al: 2.3–3.15% |
ASTM B865, ASME SB-127 |
| |
Ti: 0.35–0.85%, Fe: ≤2.0%, Mn: ≤1.5% |
NACE MR0175, DIN 17752 |
| Mechanical Properties |
Tensile Strength: 1,100–1,300 MPa |
ASTM B865, ISO 15156-3 |
| |
Yield Strength: 800–1,000 MPa |
|
| |
Elongation: ≥20% |
|
| Physical Parameters |
Density: 8.80 g/cm³ |
ISO 6892 |
| |
Melting Point: 1,288–1,343°C |
|
| |
Thermal Conductivity: 22 W/m·K |
|
Applications
-
Marine Engineering: Propeller shafts, seawater valve stems, and offshore platform fasteners.
-
Oil & Gas: Downhole drilling tools, valve trim, and H₂S-resistant pipeline components.
-
Aerospace: High-strength fasteners, turbine blades, and engine components.
-
Chemical Processing: Reactor agitators, heat exchanger tubes, and sulfuric acid handling systems.
-
Nuclear Energy: Control rod drive mechanisms and radiation-resistant instrumentation.
Q&A
Q1: How does Monel K500 compare to Monel 400 in mechanical performance?
A: Monel K500 offers 3x higher yield strength and 2x higher tensile strength due to aluminum/titanium additions and aging treatment, while maintaining equivalent corrosion resistance.
Q2: Can Monel K500 rods withstand cryogenic temperatures?
A: Yes. The alloy retains ductility and near-zero magnetic permeability at -196°C, ideal for LNG storage and superconducting applications.
Q3: What heat treatment is required for optimal performance?
A: Aging at 593–607°C for 6–16 hours followed by controlled cooling maximizes γ' phase precipitation. Stress relief annealing at 620–650°C is recommended for cold-worked rods.
Product Tags:
|
|
ASTM JIS AISI EN GB Monel K500 Rod Corrosion Resistance Images
|